Title: | Engineering of highly conductive and ultra-thin nitrogen-doped graphene films by combined methods of microwave irradiation, ultrasonic spraying and thermal annealing |
Author: | Tung, T.T. Alotaibi, F. Nine, M.J. Silva, R. Tran, D.N.H. Janowska, I. Losic, D. |
Citation: | Chemical Engineering Journal, 2018; 338:764-773 |
Publisher: | Elsevier BV |
Issue Date: | 2018 |
ISSN: | 1385-8947 1873-3212 |
Statement of Responsibility: | Tran Thanh Tung, Faisal Alotaibi, Md J. Nine, Rifat Silva, Diana N.H. Tran, Izabela Janowska, Dusan Losic |
Abstract: | We report a new method for the fabrication of highly conductive and transparent ultrathin nitrogen (N) doped graphene films from graphene inks by combining a microwave treatment, ultrasonic nebulizer coating and thermal annealing. The starting graphene oxide (GO) solution was mixed with poly(ionic liquids) (PIL) and treated with microwave (Mw) irradiation to prepare Mw-rGO@PIL inks, which is a gentle reduction of PIL-attached reduced graphene oxide (rGO). In this non-contacting heating method, the PIL was used to not only mediate microwave irradiation and prevent disorder of the graphitic structure, but also repair the lattice defects and introduce nitrogen into the graphitic structure. The ultra-thin graphene films were prepared using the nebulizer for controlling the aerosol droplet distribution of the Mw-rGO@PIL inks coated onto quartz or glass substrates. The prepared films displayed a surface resistance of ∼1.45 × 107 Ω/sq at a transparency of ∼87%. A further thermal treatment was conducted to improve the conductivity of the prepared films by annealing at a high temperature (900 °C), which allowed complete reduction of oxygen containing groups, enhanced graphitization, and reordering of the basal graphene plane and N-doping of the carbon lattice (pyrolytic PIL). The resulting thin films significantly reduced the surface resistance in the range of 1.5 × 103 to 6.2 × 103 Ω/sq at a transparency ranging from 68 to 82%, respectively. The presented method involving in situ N-doping offers a promising environmentally-friendly, low-cost and scalable manufacture of high-quality conductive N-doped graphene films. |
Keywords: | Graphene thin films; N-doped graphene; graphene inks; graphene coatings; ultrasonic spaying |
Description: | Available online 04 February 2018 |
Rights: | © 2018 Elsevier B.V. All rights reserved. |
DOI: | 10.1016/j.cej.2018.01.085 |
Grant ID: | http://purl.org/au-research/grants/arc/IH150100003 |
Published version: | http://dx.doi.org/10.1016/j.cej.2018.01.085 |
Appears in Collections: | ARC Research Hub for Graphene Enabled Industry Transformation publications Aurora harvest 3 Chemical Engineering publications |
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.